Abstract
Statement of problem
Zirconia abutments with a titanium base are promising candidates to substitute for titanium abutments based on clinical studies reporting good short-term survival rates. However, information on the long-term performance of zirconia abutments supporting ceramic crowns is scarce.
Purpose
This in vitro comparative and finite element analysis study compared the fatigue life performance of ceramic computer-aided design and computer-aided manufacturing (CAD-CAM) monolithic restorations and zirconia abutments fabricated with a chairside workflow connected to a titanium interface versus titanium abutments.
Material and methods
Twenty-two internal connection implants were divided into 2 groups, one with a zirconia abutment and monolithic ceramic zirconia crown (ZZ) and the other with a titanium abutment and zirconia crown (TiZ). They were subjected to a fatigue test to determine the fatigue limit and fatigue performance of each group as per International Organization for Standardization (ISO) 14801. Microstructural analysis of the fracture surfaces was conducted by using a scanning electron microscope (SEM). Simulations of the in vitro study were also conducted by means of finite element analysis (FEA) to assess the stress distribution over the different parts of the restoration.
Results
The fatigue limit was 250 N for the TiZ group and 325 N for the ZZ group. In both groups, the screw was the part most susceptible to fatigue and was where the failure initiated. In the zirconia abutment models, the stress on the screw was reduced.
Conclusions
Chairside CAD-CAM zirconia abutments with a titanium base supporting zirconia crowns had higher fatigue fracture resistance compared with that of titanium abutments.